±19 AWG / 0.90mm Kanthal D (1 Meter)

R40.00

In stock

Category:

Description

Kanthal D

(Resistance heating wire and resistance wire)
Kanthal D is a ferritic iron­chromium­aluminium alloy (FeCrAl alloy) for use at
temperatures up to 1300°C (2370°F). The alloy is characterized by high resistivity and
good oxidation resistance.
Kanthal D is used in home appliances and industrial furnaces. Typical applications in
home appliances include metal sheathed tubular elements for dishwashers, elements
embedded in ceramics for panel heaters, cartridge elements in metal dies, heating cables
and rope heaters in defrosting and deicing elements, mica elements used in irons, quartz
tube heaters for space heating, industrial infrared dryers, in coils on molded ceramic
fibre for boiling plates with ceramic hobs, in bead insulated coils for panel heaters, in
suspended coil elements for air heaters in laundry dryers.
In industrial applications Kanthal D is used in, for example, terminals to furnace
elements, porcupine elements for air heating, and in furnace heating elements.
CHEMICAL COMPOSITION
C % Si % Mn % Cr % Al % Fe %
Nominal composition 4.8 Bal.
Min ­ ­ ­ 20.5 ­
Max 0.08 0.7 0.5 23.5 ­
MECHANICAL PROPERTIES
Wire size Yield strength Tensile strength Elongation Hardness
Ø R R A
mm MPa MPa % Hv
1.0 485 670 23 230
4.0 450 650 18 230
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE
Temperature °C 900
MPa 34
Ultimate tensile strength ­ deformation rate 6.2 x 10 /min
Temperature °C 800 900
CREEP STRENGTH – 1% ELONGATION IN 1000 H
MPa 1.2 0.5
PHYSICAL PROPERTIES
Density g/cm 7.25
Electrical resistivity at 20°C Ω mm/ m 1.35
Poisson’s ratio 0.30
p0.2 m
­2
3
2Temperature °C 20 100 200 400 600 800 1000
YOUNG’S MODULUS
GPa 220 210 205 190 170 150 130
Temperature°C 100 200 300 400 500 600 700 800 900 1000 1100 1200 1300
TEMPERATURE FACTOR OF RESISTIVITY
Ct 1.00 1.01 1.01 1.02 1.03 1.04 1.05 1.06 1.07 1.07 1.07 1.08 1.08
Temperature °C Thermal Expansion x 10 /K
COEFFICIENT OF THERMAL EXPANSION
20 ­ 250 11
20 ­ 500 12
20 ­ 750 14
20 ­ 1000 15
Temperature °C 50 600 800 1000 1200
THERMAL CONDUCTIVITY
W m  K 11 20 22 26 27
Temperature °C 20 200 400 600 800 1000 1200
SPECIFIC HEAT CAPACITY
kJ kg  K 0.46 0.56 0.63 0.75 0.71 0.72 0.74
Melting point °C 1500
Max continuous operating temperature in air °C 1300
Magnetic properties The material is magnetic up to approximately 600°C (Curie point).
Emissivity ­ fully oxidized material 0.70
DISCLAIMER:
Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when
we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Kanthal D materials